مقاله Crystallization Behavior of Poly(ethylene succinate)Nanocomposites Containing Inorganic WS2 Nanotubes در pdf

سه‌شنبه 1 فروردین 1396 ساعت 02:31

برای دریافت اینجا کلیک کنید

مقاله Crystallization Behavior of Poly(ethylene succinate)Nanocomposites Containing Inorganic WS2 Nanotubes در pdf دارای 4 صفحه می باشد و دارای تنظیمات در microsoft word می باشد و آماده پرینت یا چاپ است

فایل ورد مقاله Crystallization Behavior of Poly(ethylene succinate)Nanocomposites Containing Inorganic WS2 Nanotubes در pdf کاملا فرمت بندی و تنظیم شده در استاندارد دانشگاه و مراکز دولتی می باشد.

این پروژه توسط مرکز مرکز پروژه های دانشجویی آماده و تنظیم شده است

توجه : در صورت  مشاهده  بهم ریختگی احتمالی در متون زیر ،دلیل ان کپی کردن این مطالب از داخل فایل ورد می باشد و در فایل اصلی مقاله Crystallization Behavior of Poly(ethylene succinate)Nanocomposites Containing Inorganic WS2 Nanotubes در pdf ،به هیچ وجه بهم ریختگی وجود ندارد


بخشی از متن مقاله Crystallization Behavior of Poly(ethylene succinate)Nanocomposites Containing Inorganic WS2 Nanotubes در pdf :

سال انتشار: 1393
محل انتشار: پانزدهمین کنگره ملی مهندسی شیمی ایران
تعداد صفحات: 4
چکیده:

Biodegradable poly(ethylene succinate) (PES)/inorganic tungstan disufide nanotubes (INT-WS2)nanocomposites were prepared through solution casting method. Crystallization behavior of PES and its nanocomposites was studied with differential scannig calorimetry (DSC) under nonisothermal condition. Effect of cooling rate and INT-WS2 content on nonisothermal melt crystallization as well as cold cystallization was investigated in detail. It was found that crystallization peak temperatures were shifted to higher temperature range by presence of INTWS2and degree of crystallinity was increased particularly at higher cooling rates. The results indicate that the nonisothermal melt crystallization of PES was enhanced by the presence of INTWS2 due to the heterogeneous nucleation effect of nanotubes. Nucleation activity for each concentration was calculated through a method suggested from Dobreva et al. The results of the nucleation activity investigation showed that the nucleation activity was influenced by the nanotube content and the sample loaded with 0.5 wt.% of WS2 exhibited the highest nucleationactivity.


دانلود این فایل


برای دریافت اینجا کلیک کنید
نظرات (0)
برای نمایش آواتار خود در این وبلاگ در سایت Gravatar.com ثبت نام کنید. (راهنما)

نام :
ایمیل :
وب/وبلاگ :
ایمیل شما بعد از ثبت نمایش داده نخواهد شد